Microstructural and tribological comparison of HVOF-sprayed and post-treated M-Mo-Cr-Si (M = Co, Ni) alloy coatings
Articolo
Data di Pubblicazione:
2007
Citazione:
Microstructural and tribological comparison of HVOF-sprayed and post-treated M-Mo-Cr-Si (M = Co, Ni) alloy coatings / Bolelli, Giovanni; Cannillo, Valeria; Lusvarghi, Luca; Montorsi, Monia; F., Pighetti Mantini; M., Barletta. - In: WEAR. - ISSN 0043-1648. - STAMPA. - 263:7-12(2007), pp. 1397-1416. [10.1016/j.wear.2006.12.002]
Abstract:
High velocity oxygen-fuel (HVOF)-spayed wear resistant Co-28%Mo-17%Cr3%Si and Ni-32%Mo-15%Cr-3%Si coating, both as sprayed and after heat treatments at 600°C for 1h, have benn studied.
Tipologia CRIS:
Articolo su rivista
Keywords:
Co alloy; Ni alloy; HVOF spraying; Pin on disk test; sliding wear; Post-treatment