Characterisation of porcelain compositions using two china clays from Cameroon

Mayouom and Ntamuka china clays, from Cameroon were used to produce porcelain bodies. Two soft porcelain formulations: PSI (withMayouom) and PSII (with Ntamuka) and one hard porcelain, PH (with both Mayouom and Ntamuka) were prepared.The maximum density and flexural resistance for these formulations were obtained at 1200 8C for PSI, 1225 8C for PSII and 1350 8C for PH.Their properties and values were, respectively, density (2.42, 2.58 and 2.59 g/cm3), water absorption (0.15, 0.15 and 0.02%), porosity (4.3, 5.3 and4.2%) and flexural strength (148, 148 and 160 MPa). In addition to varying amounts of liquid phase, the soft porcelain formulations containedmullite and quartz crystals while the hard porcelains contained quartz and more intense mullite peaks. At 1250 8C PSI and PSII presented a selfglazingphenomenon which gave significant brightness and high aesthetic quality. PH with lower alkali (especially Na+) did not self-glaze even at1400 8C. Considering the soft porcelain formulations, the higher amounts of TiO2 (0.83%) and Fe2O3 (0.31%) in PSI (with Mayoum clay) resultedin a higher sintering effect at lower temperatures, giving lower water absorption and higher resistance. Both Mayouom and Ntamuka china clayswere found to be suitable raw materials for the production of porcelain stoneware tiles. Ntamuka could also be used for the manufacture of optimalquality whitewares.